Firma Shandong SDBALLS Industry Co., LTD powstała na bazie fabryki kul stalowych Shengdian. Firma ma ponad 30 lat doświadczenia w produkcji.
ISO 3290-1 Normy międzynarodowe
NORMA ISO3290-1:2014 (KULKI STALOWE)
| Klasa precyzji | Zmiana średnicy kuli (VDws) (μm) (a) | Odchylenie od formy kulistej (tDw) (>μm) (a) | Chropowatość powierzchni (Ra) (μm) (a) | Zmiana średnicy partii kulek (VDwL) (μm) | Interwał pomiarowy (IG) | Opis preferowanego wskaźnika | Odstęp podtorowy | Opis podgrup (SG) |
|---|---|---|---|---|---|---|---|---|
| 3 | 0.08 | 0.08 | 0.01 | 0.13 | 0.5 | -5/-0.5,0,+0.5/+5 | 0.1 | -0.2,-0.1,0,0.1,0.2 |
| 5 | 0.13 | 0.13 | 0.014 | 0.25 | 1 | -5/-1,0,+1/+5 | 0.2 | -0.4,-0.2,0,0.2,0.4 |
| 10 | 0.25 | 0.25 | 0.02 | 0.5 | 1 | -9/-1,0,+1/+9 | 0.2 | -0.4,-0.2,0,0.2,0.4 |
| 16 | 0.4 | 0.4 | 0.025 | 0.8 | 2 | -10/-2,0,+2/+10 | 0.4 | -0.8,-0.4,0,0.4,0.8 |
| 20 | 0.5 | 0.5 | 0.032 | 1 | 2 | -10/-2,0,+2/+10 | 0.4 | -0.8,-0.4,0,0.4,0.8 |
| 24 | 0.6 | 0.6 | 0.04 | 1.2 | 2 | -12/-2,0,+2/+12 | 0.4 | -0.8,-0.4,0,0.4,0.8 |
| 28 | 0.7 | 0.7 | 0.05 | 1.4 | 2 | -12/-2,0,+2/+12 | 0.4 | -0.8,-0.4,0,0.4,0.8 |
| 40 | 1 | 1 | 0.06 | 2 | 4 | -16/-4,0,+4/+16 | 0.8 | -1.6,-0.8,0,0.8,1.6 |
| 60 | 1.5 | 1.5 | 0.08 | 3 | 6 | -18/-6,0,+6/+18 | 1.2 | -2.4,-1.2,0,1.2,2.4 |
| 100 | 2.5 | 2.5 | 0.1 | 5 | 10 | -40/-10,0,10/40 | 2 | -4,-2,0,2,4 |
| 200 | 5 | 5 | 0.15 | 10 | 15 | -60/-15,0,15/60 | 3 | -6,-3,0,3,6 |
Międzynarodowe standardy AFBMA
STANDARDY AFBA (USA)
| Oceny AFBMA | Zmiana średnicy/okrągłości kuli | Zmiana średnicy partii | Podstawowa tolerancja średnicy | Maksymalne przyrosty | Chropowatość powierzchni | |||||
|---|---|---|---|---|---|---|---|---|---|---|
| CALE | mikrometrów | CALE | mikrometrów | CALE | mikrometrów | CALE | mikrometrów | CALE | mikrometrów | |
| 3 | 0.000003 | 0.0762 | 0.000005 | 0.127 | ±0,00003 | 0.762 | 0.000010 | 0.254 | 0.0000005 | 0.0127 |
| 5 | 0.000005 | 0.127 | 0.000010 | 0.245 | ±0,00005 | 1.27 | 0.000010 | 0.254 | 0.0000008 | 0.02032 |
| 10 | 0.000010 | 0.254 | 0.000020 | 0.508 | ±0,00010 | 2.54 | 0.000010 | 0.254 | 0.000001 | 0.0254 |
| 15 | 0.000015 | 0.381 | 0.000030 | 0.762 | ±0,00010 | 2.54 | 0.000010 | 0.254 | 0.000001 | 0.0254 |
| 16 | 0.000016 | 0.4064 | 0.000032 | 0.8128 | ±0,00010 | 2.54 | 0.000010 | 0.254 | 0.000001 | 0.0254 |
| 24 | 0.000024 | 0.6096 | 0.000048 | 1.2192 | ±0,00010 | 2.54 | 0.000010 | 0.254 | 0.000002 | 0.0508 |
| 25 | 0.000025 | 0.635 | 0.000050 | 1.27 | ±0,00020 | 2.54 | 0.000010 | 0.254 | 0.000002 | 0.0508 |
| 45 | 0.000045 | 1.2192 | 0.000096 | 2.4384 | ±0,00030 | 5.08 | 0.000050 | 1.27 | 0.000003 | 0.0762 |
| 50 | 0.000050 | 1.27 | 0.000100 | 2.54 | ±0,00050 | 7.62 | 0.000050 | 1.27 | 0.000003 | 0.0762 |
| 100 | 0.000100 | 2.54 | 0.000200 | 5.08 | ±0,00100 | 12.7 | 0.000100 | 2.54 | 0.000005 | 0.127 |
| 200 | 0.000200 | 5.08 | 0.000400 | 10.20 | ±0,00100 | 25.4 | 0.000200 | 5.08 | 0.000008 | 0.2032 |
| 300 | 0.000300 | 7.62 | 0.000400 | 15.24 | ±0,00100 | 25.4 | 0.000300 | 7.62 | – | – |
| 500 | 0.000500 | 12.70 | 0.001000 | 25.40 | ±0,00200 | 50.8 | 0.000500 | 12.70 | – | – |
| 1000 | 0.001000 | 25.40 | 0.002000 | 50.80 | ±0,00500 | 127.0 | 0.001000 | 25.40 | – | – |
| 2000 | 0.002000 | 50.80 | 0.004000 | 101.60 | ±0,00500 | 127.0 | 0.002000 | 50.80 | – | – |
| 3000 | 0.003000 | 76.20 | 0.006000 | 152.40 | ±0,00500 | 127.0 | 0.003000 | 76.20 | – | – |
Normy międzynarodowe Din 5401
DIN 5401:2002-08 (NORMY NIEMIECKIE)
| Stopień | Klasa | Średnica nominalna Dw(mm) | Odchylenia graniczne | Zmiana średnicy kuli | Okrągłość | Chropowatość powierzchni s(6) | Zmiana średnicy partii -5 | Interwał podmierny | Podmierniki (μm) (7) | |||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| z | Do | (um)(s) | VDws Max(um) | tDws Max (um) | Ra Max(um) | VDwL/A Max(um) | IG, ST (um) | (um) | ||||
| G3 | – | – | 12.7 | ±5,32 | 0.08 | 0.08 | 0.01 | 0,13(dł.) | 0.5 | od -5 do -0,5 | 0 | od +0,5 do +5 |
| G5 | I | – | 12.7 | ±5,63 | 0.13 | 0.13 | 0.014 | 0,25(dł.) | 1 | od -5 do 1 | 0 | od+1 do+5 |
| G10 | II | – | 25.4 | ±9,75 | 0.25 | 0.25 | 0.02 | 0,50(dł.) | 1 | od 9 do 1 | 0 | od +1 do +9 |
| G16(1) | III | – | 25.4 | ±11,4 | 0.4 | 0.4 | 0.025 | 0,80(dł.) | 2 | od -10 do 2 | 0 | od +2 do +10 |
| G20(1) | III | – | 38.1 | ±11,5 | 0.5 | 0.5 | 0.032 | 1,0(dł.) | 2 | od -10 do 2 | 0 | od +2 do +10 |
| G28(1) | III | – | 50.8 | ±13,7 | 0.7 | 0.7 | 0.05 | 1,4(dł.) | 2 | od -12 do 2 | 0 | od +2 do +12 |
| G40 | III | – | 100 | ±19,0 | 1 | 1 | 0.06 | 2,0(dł.) | 4 | od 16 do 4 | 0 | od +4 do +16 |
| G80(2) | III | – | 100 | ±14,0 | 2 | 2 | 0.1 | 4,0(A) | 4 | od -12 do 4 | 0 | od +4 do +12 |
| G100n | III | – | 150 | ±47,5 | 2.5 | 2.5 | 0.1 | 5,0(dł.) | 10 | od -40 do -10 | 0 | od +10 do +40 |
| G200 | IV | – | 150 | ±72,5 | 5 | 5 | 0.15 | 10(dł.) | 10 | od -60 do -10 | 0 | od +10 do +60 |
| G300(1) | IV | – | 25.4 | ±70,0 | 10 | 10 | 0.2 | 20(A) | 20 | od -60 do -20 | 0 | od +20 do +60 |
| G300(3) | IV | 25,4 | 50.8 | ±105 | 15 | 15 | 0.2 | 30(A) | 30 | od -90 do -30 | 0 | od+30 06+01 |
| G300 | IV | 50,8 | 75 | ±140 | 20 | 20 | 0.2 | 40(A) | 40 | od -120 do -40 | 0 | od +40 do +120 |
| G500（4） | V | – | 25.4 | ±75,0 | 25 | 25 | – | 50(A) | 50 | -50 | 0 | 50 |
| G500 | V | 25,4 | 50.8 | ±112,5 | 25 | 25 | – | 75(A) | 75 | -75 | 0 | 75 |
| G500 | V | 50,8 | 75 | ±150 | 25 | 25 | – | 100(A) | 100 | -100 | 0 | 100 |
| G500 | V | 75 | 100 | ±187,5 | 32 | 32 | – | 125(A) | 125 | -125 | 0 | 125 |
| G500 | V | 100 | 125 | ±225 | 38 | 38 | – | 150(A) | 150 | -150 | 0 | 150 |
| G500 | V | 125 | 150 | ±262,5 | 44 | 44 | – | 175(A) | 175 | -175 | 0 | 175 |
| G600（4） | VI | Wszystko | Wszystko | ±200 | – | – | – | 400(A) | – | – | 0 | – |
| G700(4) | VI | Wszystko | Wszystko | ±1000 | – | – | – | 2000(A) | – | – | 0 | – |
Terminy, symbole i definicje
| TERMIN | SYMBOL | DEFINICJA |
|---|---|---|
| Średnica nominalna kuli | Dw | Wartość średnicy służąca do ogólnej identyfikacji rozmiaru kuli |
| Średnica pojedynczej kuli | Dws | Odległość między dwiema równoległymi płaszczyznami stycznymi do rzeczywistej powierzchni piłki. |
| Średnia średnica kuli | Dwm | Średnia arytmetyczna największej i najmniejszej pojedynczej średnicy kuli |
| Zmiana średnicy kuli | VDws | Różnica między największą i najmniejszą średnicą pojedynczej kuli |
| Odchylenie od formy kulistej | tDw | Największa odległość promieniowa w dowolnej płaszczyźnie równikowej między najmniejszą sferą opisaną i największą sferą wpisaną, których środki znajdują się we wspólnym środku najmniejszej sfery kwadratowej. |
| Los piłek | Określa ilość kulek wyprodukowanych w warunkach uznanych za jednolite i traktowanych jako całość | |
| Średnia średnica partii kulek | DwmL | Średnia arytmetyczna średnich średnic największej kuli i najmniejszej kuli w partii kul. |
| Zmiana średnicy partii kulek | VDwL | Różnica pomiędzy średnią średnicą największej kuli i najmniejszej kuli w partii kul. |
| Stopień piłki | G | Specyficzna kombinacja tolerancji wymiarów, kształtu, chropowatości powierzchni i sortowania kulek. Klasa kulek jest oznaczona literą G i liczbą. |
| Wskaźnik kulkowy | S | Wartość, o jaką średnica średnia partii kulek powinna różnić się od średnicy nominalnej kulki, przy czym wartość ta jest wartością z ustalonej serii. Każdy rozmiar kalibru kulek stanowi całkowitą wielokrotność przedziału kalibru kulek ustalonego dla danej klasy kulek. Rozmiar kalibru kulek, w połączeniu z klasą kulek i średnicą nominalną, należy traktować jako najdokładniejszą specyfikację rozmiaru kulek, którą klient powinien wykorzystać do celów składania zamówienia. |
| Odchylenie partii kulek od grubości kulek | ΔS | Różnica między średnią średnicą partii kulek a sumą nominalnej średnicy kulki i grubości kulki: ΔS = DwmL - (Dw+S). |
| Podmiernik kulkowy | – | Wartość z ustalonego szeregu wartości, która jest najbliższa rzeczywistemu odchyleniu od średnicy kulki w partii kulek. Każda podśrednica kulki stanowi całkowitą wielokrotność przedziału podśrednicy kulki ustalonego dla danego gatunku kulek. Podśrednica kulki, w połączeniu z nominalną średnicą kulki i grubością kulki, jest używana przez producentów kulek do oznaczenia średniej średnicy partii kulek i nie powinna być stosowana przez klientów w celu składania zamówień. |
| Twardość | Miara odporności na penetrację, oznaczana określonymi metodami | |
| Chropowatość powierzchni | Ra | Nierówności powierzchni występujące w stosunkowo niewielkich odstępach, na które zwykle składają się nierówności wynikające ze stosowanej metody produkcji i/lub innych czynników. Nierówności te rozpatruje się w granicach zdefiniowanych konwencjonalnie, np. w granicach długości próbki. |
| Falistość | Nierówności powierzchni o losowym lub okresowym odchyleniu od idealnej formy sferycznej. Zaleca się ocenę falistości jako amplitudy prędkości. W praktyce składowe falistości są oddzielane od powierzchni rzeczywistej za pomocą analizatora falistości (filtrów). |
Potrzebujesz produktów wysokiej jakości? Jesteśmy gotowi Ci je dostarczyć.
Oferujemy pełną gamę precyzyjnych kulek wykonanych z różnych materiałów, gwarantujących spójną jakość i niezawodną wydajność w różnych zastosowaniach przemysłowych.
SHANDONG SDBALLS INDUSTRY CORP LTD.
Tabela konwersji
Firma Shandong SDBALLS Industry Co., LTD powstała na bazie fabryki kul stalowych Shengdian. Firma ma ponad 30 lat doświadczenia w produkcji.
Skład chemiczny materiału
| Stal | %C | %Si | %Mn | %P | %S | %Cr | %Ni | %N | %Mo | %Ti |
|---|---|---|---|---|---|---|---|---|---|---|
| AISI 1010/1015 | 0.08-0.18 | 0.10-0.35 | 0.30-0.60 | 0,040 maks. | 0,050 maks. | – | – | – | – | – |
| AISI 1085 | 0.80-0.93 | 0.10-0.35 | 0.70-1.00 | 0,040 maks. | 0,050 maks. | – | – | – | – | – |
| AISI 52100 | 0.95-1.10 | 0,35 maks. | 0.20-0.50 | 0,025 maks. | 0,025 maks. | 1.30-1.60 | – | – | – | – |
| AISI 302/304/304L | 0,150 maks. | 1,00 maks. | 2,00 maks. | 0,045 maks. | 0,030 maks. | 17.00-20.00 | 8.00-10.50 | 0,100 maks. | – | – |
| AISI 316/316L | 0,080 maks. | 1,00 maks. | 2,00 maks. | 0,045 maks. | 0,030 maks. | 16.00-18.00 | 10.00-14.00 | – | 2.00-3.00 | – |
| AISI 316Ti | 0,080 maks. | 0,75 maks. | 2,00 maks. | 0,045 maks. | 0,030 maks. | 16.00-18.00 | 10.00-14.00 | 0,100 maks. | 2.00-3.00 | 5x%C-0,70 |
| AISI 420(ABC) | 0.16-0.50 | 1,00 maks. | 1,50 maks. | 0,040 maks. | 0,030 maks. | 12.00-14.50 | – | – | – | – |
| AISI 440C | 0.95-1.20 | 1,00 maks. | 1,00 maks. | 0,040 maks. | 0,030 maks. | 16.00-18.00 | – | – | 0,75 maks. | – |
Wykres konwekcji materiału
| USA | CHN | Włochy | Wielka Brytania | GER | FRA | Rosja | Japonia |
|---|---|---|---|---|---|---|---|
| 1015 | 15 | C15 | 080M15 | 1.1141 | XC12 | 15 | S15C |
| 1085 | 82B | C90 | C85S | 1.1269 | XC90 | 85 (A) | SWRH87B |
| 52100 | GCr15 | 100Cr6 | 534A99 | 1.3505 | 100C6 | 9Ch1 | SUJ2 |
| 201 | 1Cr17Mn6Ni5N | – | 201 S 01 | 1.4372 | Z12CMN17-07Az | 14Ch18N4G4L | SUS 201 |
| 304 | 0Cr18Ni9 | X5CrNi18-10 | 304S15 | 1.4301 | Z7CN18-09 | 08KH18N10 | SUS304 |
| 304L | 00Cr19Ni10 | X2CrNi18-9 | 304S11 | 1.4307 | Z3CN18-10 | 04KH18N10 | SUS304L |
| 316 | 0Cr17Ni12Mo2 | X5CrNiMo1712 | 316S16 | 1.4401 | Z6CND17.11 | 08KH16N11M3 | SUS316 |
| 316L | 0Cr18Ni12Mo2Ti | X2CrNiMo1712 | 316S11 | 1.4404 | Z3CND17-11-02 | 03KH17N14M2 | SUS316L |
| 420C | 4Cr13 | X46Cr13 | – | 1.4034 | Z 34 C 14 | 40 Kh 13 | – |
Tabela rozmiarów i wagi
| ROZMIAR | Waga | Q/KG | |
|---|---|---|---|
| cal | mm | 1000 kulek w kg | 52100 |
| 0.5 | 0.0005 | 1960784 | |
| 0.6 | 0.0008 | 1135074 | |
| 1/32′ | 0.794 | 0.00204 | 490196 |
| 0.8 | 0.00209 | 478927 | |
| 1 | 0.00408 | 245158 | |
| 1.2 | 1.2 | 0.00705 | 141884 |
| 1.5 | 0.01377 | 72124 | |
| 1/16′ | 1.5875 | 0.016 | 60843 |
| 5/64′ | 1.9844 | 0.032 | 31500 |
| 2 | 0.033 | 30427 | |
| 3/32′ | 2.381 | 0.055 | 18058 |
| 2.5 | 0.064 | 15612 | |
| 7/64′ | 2.778 | 0.087 | 11478 |
| 3 | 0.111 | 9035 | |
| 1/8′ | 3.175 | 0.131 | 7622 |
| 3.5 | 0.176 | 5689 | |
| 5/32′ | 3.969 | 0.256 | 3902 |
| 4 | 0.262 | 3811 | |
| 4.5 | 0.374 | 2677 | |
| 3/16′ | 4.763 | 0.443 | 2258 |
| 5 | 0.513 | 1951 | |
| 7/32 | 5.556 | 0.703 | 1422 |
| 15/64′ | 5.953 | 0.866 | 1155 |
| 6 | 0.886 | 1129 | |
| 1/4′ | 6.35 | 1.049 | 953 |
| 17/64′ | 6.747 | 1.259 | 794 |
| 7 | 1.406 | 711 | |
| 9/32′ | 7.144 | 1.495 | 669 |
| 5/16′ | 7.938 | 2.053 | 487 |
| ROZMIAR | Waga | Q/KG | |
|---|---|---|---|
| cal | mm | 1000 kulek w kg | 52100 |
| 8 | 2.101 | 476 | |
| 11/32′ | 8.731 | 2.732 | 366 |
| 9 | 2.994 | 334 | |
| 3/8′ | 9.525 | 3.546 | 282 |
| 10 | 4.115 | 243 | |
| 13/32′ | 10.319 | 4.505 | 222 |
| 11 | 5.464 | 183 | |
| 7/16′ | 11.113 | 5.65 | 177 |
| 29/64′ | 11.509 | 6.25 | 160 |
| 15/32′ | 11.906 | 6.944 | 144 |
| 12 | 7.092 | 141 | |
| 31/64′ | 12.303 | 7.634 | 131 |
| 1/2′ | 12.7 | 8.403 | 119 |
| 13 | 9.072 | 111 | |
| 17/32′ | 13.494 | 10.101 | 99 |
| 14 | 11.236 | 89 | |
| 9/16′ | 14.288 | 11.905 | 84 |
| 15 | 13.889 | 72 | |
| 19/32′ | 15.081 | 14.085 | 71 |
| 5/8′ | 15.875 | 16.393 | 61 |
| 16 | 16.667 | 60 | |
| 21/32′ | 16.669 | 18.868 | 53 |
| 17 | 20 | 50 | |
| 11/16′ | 17.463 | 21.739 | 46 |
| 18 | 23.809 | 42 | |
| 23/32′ | 18.256 | 25 | 40 |
| 3/4′ | 19.05 | 28.571 | 35 |
| 25/32′ | 19.844 | 32.258 | 31 |
| 20 | 32.787 | 30.5 | |
| ROZMIAR | Waga | Q/KG | |
|---|---|---|---|
| cal | mm | 1000 kulek w kg | 52100 |
| 27/32′ | 21.431 | 40 | 25 |
| 22 | 43.478 | 23 | |
| 7/8′ | 22.225 | 45.455 | 22 |
| 23 | 50 | 20 | |
| 29/32′ | 23.019 | 50 | 20 |
| 15/16′ | 23.813 | 55.556 | 18 |
| 24 | 56.689 | 17.64 | |
| 31/32′ | 24.606 | 61.087 | 16.37 |
| 25 | 64.061 | 15.61 | |
| 1′ | 25.4 | 67.204 | 14.88 |
| 26 | 72.046 | 13.88 | |
| 1,1/16′ | 26.988 | 80.58 | 12.41 |
| 28 | 90.009 | 11.11 | |
| 1,1/8′ | 28.575 | 95.694 | 10.45 |
| 30 | 110.742 | 9.03 | |
| 1,3/16′ | 30.163 | 112.486 | 8.89 |
| 1,1/4′ | 31.75 | 131.234 | 7.62 |
| 32 | 134.409 | 7.44 | |
| 1,5/16′ | 33.338 | 151.976 | 6.58 |
| 34 | 161.29 | 6.2 | |
| 1,3/8′ | 34.925 | 174.825 | 5.72 |
| 35 | 176.056 | 5.68 | |
| 36 | 191.571 | 5.22 | |
| 1,7/16′ | 36.513 | 199.601 | 5.01 |
| 38 | 225.225 | 4.44 | |
| 1,1/2′ | 38.1 | 226.757 | 4.41 |
| 1,9/16′ | 39.688 | 256.41 | 3.9 |
| 40 | 262.467 | 3.81 | |
| 1,5/8′ | 41.275 | 288.184 | 3.47 |
| ROZMIAR | Waga | Q/KG | |
|---|---|---|---|
| cal | mm | 1000 kulek w kg | 52100 |
| 1.3/4 | 44.45 | 359.712 | 2.78 |
| 45 | 373.134 | 2.68 | |
| 1.13/16 | 46.038 | 400 | 2.5 |
| 1,7/8′ | 47.625 | 442.478 | 2.26 |
| 1.15/16 | 49.212 | 485.437 | 2.06 |
| 50 | 512.821 | 1.95 | |
| 2′ | 50.8 | 537.634 | 1.86 |
| 2,1/8′ | 53.975 | 645.161 | 1.55 |
| 55 | 680.272 | 1.47 | |
| 2,1/4′ | 57.15 | 763.359 | 1.31 |
| 60 | 884.956 | 1.13 | |
| 2.3/8 | 60.325 | 892.857 | 1.12 |
| 2,1/2′ | 63.5 | 1052.63 | 0.95 |
| 70 | 1408.45 | 0.71 | |
| 75 | 1724.13 | 0.58 | |
| 3′ | 76.2 | 1818.18 | 0.55 |
| 3.1/8 | 79.375 | 2040.81 | 0.49 |
| 80 | 2040.81 | 0.47 | |
| 3,1/4′ | 82.55 | 2325.58 | 0.43 |
| 3.1/2 | 88.9 | 2857.14 | 0.35 |
| 90 | 3030.3 | 0.33 | |
| 3,3/4′ | 95.25 | 3571.42 | 0.28 |
| 100 | 4166.66 | 0.24 | |
| 4′ | 101.6 | 4347.8 | 0.23 |
| 110 | 5555.55 | 0.18 | |
| 120 | 7142.85 | 0.14 | |
| Podana powyżej waga odnosi się do kulek stalowych SAE52100 o wadze 1 kg = 2,205 1 lbs (USA) | |
| Współczynnik mnożenia pozwalający uzyskać przybliżoną wagę 1000 piłek w kg; dla innych materiałów podano poniżej. | |
| Tworzywo | Współczynnik mnożenia |
| Stal węglowa | 1.004 |
| Stal nierdzewna AISI 302/304 | 1.011 |
| Stal nierdzewna AISI 316 | 1.025 |
| Stal nierdzewna AISI 420/440 | 0.979 |
| Szkło | 0.344 |
Czat o konwersji twardości
| Rada Praw Człowieka | HRA | HR15N | HR30N | HR45N | Wysokiego napięcia | HB30D2 | k10, 2k5, 4k2,5 mm |
|---|---|---|---|---|---|---|---|
| 17 | 67.3 | 37.9 | 15.6 | 211 | 211 | 4.15 | |
| 17.5 | 67.6 | 38.4 | 16.2 | 214 | 214 | 4.13 | |
| 18 | 67.8 | 38.9 | 16.8 | 216 | 216 | 4.11 | |
| 18.5 | 68 | 39.3 | 17.4 | 218 | 218 | 4.09 | |
| 19 | 68.3 | 39.8 | 18 | 221 | 220 | 4.07 | |
| 19.5 | 68.5 | 40.3 | 18.6 | 223 | 222 | 4.05 | |
| 20 | 68.8 | 40.7 | 19.2 | 226 | 225 | 4.03 | |
| 20.5 | 69 | 41.2 | 19.8 | 229 | 227 | 4.02 | |
| 21 | 69.3 | 41.7 | 20.4 | 231 | 227 | 4 | |
| 21.5 | 69.5 | 42.2 | 21 | 234 | 232 | 3.97 | |
| 22 | 69.8 | 42.6 | 21.5 | 237 | 234 | 3.95 | |
| 22.5 | 70 | 43.1 | 22.1 | 240 | 237 | 3.93 | |
| 23 | 70.3 | 43.6 | 22.7 | 243 | 240 | 3.91 | |
| 23.5 | 70.6 | 44 | 23.3 | 246 | 242 | 3.89 | |
| 24 | 70.8 | 44.5 | 23.9 | 249 | 245 | 3.87 | |
| 24.5 | 71.1 | 45 | 24.5 | 252 | 248 | 3.85 | |
| 25 | 71.4 | 45.5 | 25.1 | 255 | 251 | 3.83 | |
| 25.5 | 71.6 | 45.9 | 25.7 | 258 | 254 | 3.8 | |
| 26 | 71.9 | 46.4 | 26.3 | 261 | 257 | 3.78 | |
| 26.5 | 72.2 | 46.9 | 26.9 | 264 | 260 | 3.76 | |
| 27 | 72.4 | 47.3 | 27.5 | 268 | 263 | 3.74 | |
| 27.5 | 72.7 | 47.8 | 28.1 | 271 | 266 | 3.72 | |
| 28 | 73 | 48.3 | 28.7 | 274 | 269 | 3.7 | |
| 28.5 | 73.3 | 48.7 | 29.3 | 278 | 273 | 3.67 | |
| 29 | 73.5 | 49.2 | 29.9 | 281 | 276 | 3.65 | |
| 29.5 | 73.8 | 49.7 | 30.5 | 285 | 280 | 3.63 | |
| 30 | 74.1 | 50.2 | 31.1 | 298 | 283 | 3.61 | |
| 30.5 | 74.4 | 50.6 | 31.7 | 292 | 287 | 3.59 | |
| 31 | 74.7 | 51.1 | 32.3 | 296 | 291 | 3.56 | |
| 31.5 | 74.9 | 51.6 | 32.9 | 300 | 294 | 3.54 | |
| 32 | 75.2 | 52 | 33.5 | 304 | 298 | 3.52 | |
| 32.5 | 75.5 | 52.5 | 34.1 | 308 | 302 | 3.5 | |
| 33 | 75.8 | 53 | 34.7 | 312 | 306 | 3.48 | |
| 33.5 | 76.1 | 53.4 | 35.3 | 316 | 310 | 3.46 | |
| 34 | 76.4 | 53.9 | 35.9 | 320 | 314 | 3.43 | |
| 34.5 | 76.7 | 54.4 | 36.5 | 324 | 318 | 3.41 | |
| 35 | 77 | 54.8 | 37 | 329 | 323 | 3.39 | |
| 35.5 | 77.2 | 55.3 | 37.6 | 333 | 327 | 3.37 | |
| 36 | 77.5 | 55.8 | 38.2 | 338 | 332 | 3.34 | |
| 36.5 | 77.8 | 56.2 | 38.8 | 342 | 336 | 3.32 | |
| 37 | 78.1 | 56.7 | 39.4 | 347 | 341 | 3.3 | |
| 37.5 | 78.4 | 57.2 | 40 | 352 | 345 | 3.28 | |
| 38 | 78.7 | 57.6 | 40.6 | 357 | 350 | 3.26 | |
| 38.5 | 79 | 58.1 | 41.2 | 362 | 355 | 3.24 | |
| 39 | 70 | 79.3 | 58.6 | 41.8 | 367 | 360 | 3.21 |
| 39.5 | 70.3 | 79.6 | 59 | 42.4 | 372 | 365 | 3.19 |
| 40 | 70.5 | 79.9 | 59.5 | 43 | 377 | 370 | 3.17 |
| 40.5 | 70.8 | 80.2 | 60 | 43.6 | 382 | 375 | 3.15 |
| 41 | 71.1 | 80.5 | 60.4 | 44.2 | 388 | 380 | 3.13 |
| 41.5 | 71.3 | 80.8 | 60.9 | 44.8 | 393 | 385 | 3.11 |
| 42 | 71.6 | 81.1 | 61.3 | 45.4 | 399 | 391 | 3.09 |
| 42.5 | 71.8 | 81.4 | 61.8 | 45.9 | 405 | 396 | 3.07 |
| 43 | 72.1 | 81.7 | 62.3 | 46.5 | 411 | 401 | 3.05 |
| 43.5 | 72.4 | 82 | 62.7 | 47.1 | 417 | 407 | 3.03 |
| 44 | 72.6 | 82.3 | 63.2 | 47.7 | 423 | 413 | 3.01 |
| 44.5 | 72.9 | 82.6 | 63.6 | 48.3 | 429 | 418 | 2.99 |
| 45 | 73.2 | 82.9 | 64.1 | 48.9 | 436 | 424 | 2.97 |
| 45.5 | 73.4 | 83.2 | 64.6 | 49.5 | 443 | 430 | 2.95 |
| 46 | 73.7 | 83.5 | 65 | 50.1 | 449 | 436 | 2.93 |
| 46.5 | 73.9 | 83.7 | 65.5 | 50.7 | 456 | 442 | 2.91 |
| 47 | 74.2 | 84 | 65.9 | 51.2 | 463 | 449 | 2.89 |
| 47.5 | 74.5 | 84.3 | 66.4 | 51.8 | 470 | 455 | 2.87 |
| 48 | 74.7 | 84.6 | 66.8 | 52.4 | 478 | 461 | 2.85 |
| 48.5 | 75 | 84.9 | 67.3 | 53 | 485 | 468 | 2.83 |
| 49 | 75.3 | 85.2 | 67.7 | 53.6 | 493 | 474 | 2.81 |
| 49.5 | 75.5 | 85.5 | 68.2 | 54.2 | 501 | 481 | 2.79 |
| 50 | 75.8 | 85.7 | 68.6 | 54.7 | 509 | 488 | 2.77 |
| 50.5 | 76.1 | 86 | 69.1 | 55.3 | 417 | 494 | 2.75 |
| 51 | 76.3 | 86.3 | 69.5 | 55.9 | 525 | 501 | 2.73 |
| 51.5 | 76.6 | 86.6 | 70 | 56.5 | 534 | ||
| 52 | 76.9 | 86.8 | 70.4 | 57.1 | 543 | ||
| 52.5 | 77.1 | 87.1 | 70.9 | 57.6 | 551 | ||
| 53 | 77.4 | 87.4 | 71.3 | 58.2 | 561 | ||
| 53.5 | 77.7 | 87.6 | 71.8 | 58.8 | 570 | ||
| 54 | 77.9 | 87.9 | 72.2 | 59.4 | 579 | ||
| 54.5 | 78.2 | 87.6 | 72.6 | 59.9 | 589 | ||
| 55 | 78.5 | 88.4 | 73.1 | 60.5 | 599 | ||
| 55.5 | 78.7 | 88.6 | 73.5 | 61.1 | 609 | ||
| 56 | 79 | 88.9 | 73.9 | 61.7 | 620 | ||
| 56.5 | 79.3 | 89.1 | 74.4 | 62.2 | 631 | ||
| 57 | 79.5 | 89.4 | 74.8 | 62.8 | 642 | ||
| 57.5 | 79.8 | 89.6 | 75.2 | 63.4 | 653 | ||
| 58 | 80.1 | 89.8 | 75.6 | 63.9 | 664 | ||
| 58.5 | 80.3 | 90 | 76.1 | 64.5 | 676 | ||
| 59 | 80.6 | 90.2 | 76.5 | 65.1 | 688 | ||
| 59.5 | 80.9 | 90.4 | 76.9 | 65.6 | 700 | ||
| 60 | 81.2 | 90.6 | 77.3 | 66.2 | 713 | ||
| 60.5 | 81.4 | 90.8 | 77.7 | 66.8 | 726 | ||
| 61 | 81.7 | 91 | 78.1 | 67.3 | 739 | ||
| 61.5 | 82 | 91.2 | 78.6 | 67.9 | 752 | ||
| 62 | 82.2 | 91.4 | 79 | 68.4 | 766 | ||
| 62.5 | 82.5 | 91.5 | 79.4 | 69 | 780 | ||
| 63 | 82.8 | 91.7 | 79.8 | 69.5 | 795 | ||
| 63.5 | 83.1 | 91.8 | 80.2 | 70.1 | 810 | ||
| 64 | 83.3 | 91.9 | 80.6 | 70.6 | 825 | ||
| 64.5 | 83.6 | 92.1 | 81 | 71.2 | 840 | ||
| 65 | 83.9 | 92.2 | 81.3 | 71.7 | 856 | ||
| 65.5 | 84.1 | 872 | |||||
| 66 | 84.4 | 889 | |||||
| 66.5 | 84.7 | 906 | |||||
| 67 | 85 | 923 | |||||
| 67.5 | 85.2 | 941 | |||||
| 68 | 85.5 | 959 | |||||
| 68.5 | 85.8 | 978 | |||||
| 69 | 86.1 | 997 | |||||
| 69.5 | 86.3 | 1017 | |||||
| 70 | 86.6 | 1037 |